萬向節聯軸器材質(zhi)自(zi)(zi)(zi)(zi)由(you)鍛(duan)(duan)造(zao)(zao)(zao)(zao)所用工(gong)(gong)具(ju)和(he)設(she)備簡單，通用性好，成本(ben)低。同鑄造(zao)(zao)(zao)(zao)毛坯相(xiang)比，自(zi)(zi)(zi)(zi)由(you)鍛(duan)(duan)消除(chu)了縮孔、 縮松、氣孔等缺陷，使毛坯具(ju)有(you)(you)更高的力學性能。鍛(duan)(duan)件形狀簡單，操(cao)作(zuo)靈(ling)活。因此，它(ta)在(zai)重(zhong)(zhong)型機器及重(zhong)(zhong)要零件的制造(zao)(zao)(zao)(zao)上有(you)(you)特(te)別(bie)重(zhong)(zhong)要的意義。自(zi)(zi)(zi)(zi)由(you)鍛(duan)(duan)造(zao)(zao)(zao)(zao)分手(shou)工(gong)(gong)自(zi)(zi)(zi)(zi)由(you)鍛(duan)(duan)和(he)機器自(zi)(zi)(zi)(zi)由(you)鍛(duan)(duan)。手(shou)工(gong)(gong)自(zi)(zi)(zi)(zi)由(you)鍛(duan)(duan)生(sheng)(sheng)產(chan)效率低，勞動強度大(da)，僅用于修配(pei)或簡單、小型、小批鍛(duan)(duan)件的生(sheng)(sheng)產(chan)。在(zai)現代工(gong)(gong)業生(sheng)(sheng)產(chan)中(zhong)，機器自(zi)(zi)(zi)(zi)由(you)鍛(duan)(duan)已成為鍛(duan)(duan)造(zao)(zao)(zao)(zao)生(sheng)(sheng)產(chan)的主要方法，在(zai)重(zhong)(zhong)型機械制造(zao)(zao)(zao)(zao)中(zhong)，它(ta)具(ju)有(you)(you)特(te)別(bie)重(zhong)(zhong)要的作(zuo)用。

聯(lian)軸器(qi)鍛(duan)件(jian)材料(liao)需(xu)有檢驗合(he)格證書，如(ru)需(xu)代用材料(liao)，須(xu)征得(de)需(xu)方同(tong)意，并有書面(mian)文件(jian)。鍛(duan)件(jian)應(ying)(ying)在具有足(zu)夠(gou)噸位的(de)水壓或(huo)鍛(duan)錘上進行鍛(duan)造(zao)(zao)(zao)，鍛(duan)造(zao)(zao)(zao)應(ying)(ying)有足(zu)夠(gou)的(de)鍛(duan)造(zao)(zao)(zao)比，使整(zheng)個截面(mian)鍛(duan)透(tou)，以(yi)獲得(de)均勻性組織。鍛(duan)件(jian)的(de)軸線應(ying)(ying)相(xiang)當鋼錠的(de)中(zhong)心線。鍛(duan)件(jian)應(ying)(ying)由鋼錠或(huo)鋼坯鍛(duan)造(zao)(zao)(zao)成形。允(yun)許倍(bei)尺鍛(duan)造(zao)(zao)(zao)，一般(ban)應(ying)(ying)作分離(li)熱處理。

熱處理和機械加工要求：

• 鍛造后熱處理：鍛件鍛后應進行預熱處理，以改善組織和可加工性。
  

• 粗加工：鍛件性能熱處理前應進行粗加工，留小加工余量。
  

• 性能熱處理：鍛件應進行淬火和回火，以達所要求的性能。
  

• 性能熱處理后的機加工：機械性能合格后，鍛件加工到需方提供的圖樣所規定的尺寸和表面粗糙度。但如果任一表面的切削量超過5mm時，鍛件必須進行除應力處理。
  

• 除應力處理：鍛件除應力的溫度應低于回火溫度30°，保溫后，應緩慢冷卻。若除應力溫度不低于回火溫度30°時， 除應力后鍛件應重新進行機械性能試驗。